Image forming method and image forming material

ABSTRACT

An image forming method wherein an aqueous dispersion is prepared in a vessel of an apparatus. The aqueous dispersion contains an electrodeposition material including a fine particle coloring material, and a polymer which is chemically dissolved, or is deposited and precipitated, by a change in pH. The electrodeposition material is deposited and precipitated by changing the pH value of the aqueous dispersion in the vicinity of the image supporting surface of the image supporting member. The polymer in the electrodeposition material has both hydrophobic groups and hydrophilic groups, the proportion of number of the hydrophobic groups to the total number of hydrophilic groups and the hydrophobic groups in the polymer is in the range of from 40 to 80%, 50% or more of the hydrophilic groups can reversibly change from hydrophilic groups to hydrophobic groups due to a change in pH value.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to an image forming method wherein animage is formed by electrochemically insolubilizing an image formingmaterial by application of electric current using an aqueous coloringmaterial dispersion, particularly an aqueous fine particle coloringmaterial dispersion, and an image forming material used in this method.

2. Description of the Related Art

Many methods of using a liquid image forming material are known in imagerecording technologies used in offices. For example, silver saltrecording technology, ink jet recording technology, andelectrophotographic recording technology.

Printing technology are known using silver salt has been published inTanemura Hatsumi et al., “HIGH QUALITY COLOR COPYING SYSTEM BY SILVERSALT PHOTOGRAPHIC METHOD”, Preprint of Japan Hardcopy '89, p229.Printing technology using liquid development electrophotographictechnology has been published in E. B. Caruthers et al., “Modeling ofLiquid Toner Electrical Characteristics”, Proceedings of IS & T 10thInt'l. Congress on Advances in Non-Impact Printing Technologies,p204('94). Printing technology using ink jet recording has beenpublished in many technical reports such as Usui Minoru, “Development ofa New Process MACH”, Preprint of Japan Hardcopy '96, p161.

In other conventional printing technologies, the recording method usingsilver salt does not present problems of image quality or imagefastness. However, the use of this method in an office is associatedwith problems, because this method is based on a printing process whichinvolves a chemical reaction using chemically active agents andproducing waste. The problems of ink jet printing technology are thathigh resolution cannot be easily obtained because of problems created bythe small nozzle diameter in printing reliability; and that imagefastness, safety, and printability on plain paper are inadequate,because the image forming material is usually an aqueous dye.Electrophotographic technology has no problem with regard to imagequality, printability on plain paper, and high image fastness comparableto that of a printed product. However, electrophotographic technologyhas the disadvantages that a large amount of energy is consumed in thefixing unit of an electrophotographic apparatus; that the size of theapparatus is large because of the complicated printing process; and thatsafety and reliability problems arise.

There are also disclosed as conventional technologies resembling theimage forming method of the present invention, for example, a technologyusing an electrodepositable liquid in which a coloring material isdispersed in an electrically insulating liquid so as to generate anelectrical double layer in Japanese Patent Application Laid-Open (JP-A)No. 7-181750 and Japanese Patent Application Publication (JP-B) No.7-54407; “Fine Pattern Forming Method” relating to an electrodepositionprinting technology using a printing plate comprising an electricallyconductive substrate with an insulating pattern formed thereon in JP-ANo. 4-9902; and “Electrodeposition Offset PrintingMethodand PrintingPlate” in JP-A No. 6-293125, respectively.

Meanwhile, properties required for printing technology for use inoffices are, for example, a color high-quality image of 600 DPI orhigher and multi-gradation, capability of printing on plain paper, highimage fastness comparable to that of a printed product, high safety ofthe recorded matter and the recording apparatus, almost no wasteproduced, and low running cost. However, conventional technologies havevarious defects as described above, and none of the technologiesdescribed in the above-described various patents documents usingelectrodeposition property have reached the level at which theabove-mentioned requirements are completely satisfied.

In order to obtain an image having a high quality (resolution of a levelof 1000 DPI, good color reproduction, and multi-gradation), thethickness of the image structure is preferably 2 microns or less, andmore preferably 1 micron or less, in the light of the relationshipbetween the range of color reproduction and the sharpness of image.Accordingly, the average particle size of the image forming material, asthe element which imparts structure to the image, needs to be of asub-micron order. However, since a fluidity problem arises if theaverage particle size of the image forming material is 5 μm or less,practical use of a powdery image forming material is difficult. Incomparison, when viewed from this standpoint, the use of a liquid imageforming material would be effective. In the step of forming an imagehaving a size of the order of several microns, it is technicallydifficult to accurately control the image formation of the particles ofimage forming material if the size of the particles is very small.Accordingly, use of aqueous solution of a dye having a size of molecularorder which is a minimum fine particle as an electrodeposition materialis considered to be a very effective technical method also from theviewpoint of an accurate coloring material controlling method.

The electrophotographic technology, which uses a developer in the formof an electrically insulating liquid and which is disclosed in, forexample, JP-A No. 7-181750, is advantageous in that high resolution canbe obtained because the size of the image forming material is of asub-micron order; and printability on plain paper is high. However,since this method uses a developer comprising a hydrocarbon solvent, thesolvent vapor presents a serious safety problem. Therefore, the use ofsuch a developer is strictly regulated in some countries.

The electrodeposition printing technology using a printing platecomprising an electrically conductive substrate and an electricallyinsulating pattern formed thereon as described in patents such as JP-ANo. 4-9902 and the like is disadvantageous in that it is difficult tochange image patterns for each printing because the process iscomplicated, for example, the non-image portion of an insulating resistneeds to be prepared beforehand by photolithography. Other disadvantagesare as follows. Since the apparatus to be used in this method isprovided with a high precision, has a large size, involves many stepsand produces a large amount of waste, it necessarily follows that theplace where the apparatus is installed for printing is limited to afactory well equipped with facilities. Further, since the hysteresis ofthe image forming step tends to remain on the substrate, minute imagerecording cannot be fully reproduced. Furthermore, since the imageforming portions in this method are concave, it is difficult to obtain ahigh quality image, because the selective adherence of particles to theimage portions by electrophoresis is weakened and a large proportion ofthe liquid component of the image forming liquid material tends toremain on the image forming portions thus reducing the viscosity of theimage forming material in the image forming portions, and consequentlythe image forming material in the image forming portions is liable toflow or cause a cohesive failure in the transfer step. Further, any ofthem is a technology for making a printing plate used for forming finepatterns, and is not a technology of recording an image directly on arecording medium.

As described above, technologies of conventional image forming methodscannot satisfy the properties, i.e., a high degree of safety using asimple apparatus, required for printing for use in offices.

In order to realize a high quality (600 DPI or more andmulti-gradation), the minimum unit size of image forming material ispreferably 1 micron or less. Therefore, it is necessary to use a liquidimage forming material which can contain fine particles of a coloringmaterial. When the installation of an apparatus in an office is takeninto consideration, the liquid for use in the image forming materialneeds to be extremely safe. Preferably, water should be selected as theliquid as there are no problems regarding its safety. A printing processusing a printing plate which cannot be regenerated is not suitable foruse in an office, because office printing technology is required toprepare various sorts of printed matters in small quantities, easily,and at a low cost. Therefore, the market has a liking for a system whichcomprises inputting an image signal to produce image information forevery printing and the image information as an image of the imageforming material is transferred for recording on various recording mediasuch as plain paper and the like corresponding to various need of uses.

In addition, when such factors as the fastness and high optical densityof an image, and the safety from the fact that the color formingmaterial is not taken into human body are taken into consideration, itis necessary to use a coloring material comprising a pigment. It is alsonecessary to keep the energy consumption to a minimum in the printingstep.

Further, a pH regulator is often added to an aqueous dispersion forreducing energy required for deposition of an electrodepositionmaterial. It has been known that if this pH regulator remains in thedeposited electrodeposition film, various problems occur such asre-dissolution of an image (electrodeposition film) and the like fromthe viewpoint of image stability.

The present invention has been made to address the aforementionedproperties. Therefore it is an object of the present invention to obtaina high-quality image by use of an electrodeposition material containinga pigment coloring material, particularly fine particles of a coloringmaterial and to provide an image forming method which is able to form animage even by application of voltage wherein potential differencebetween image formation part and a reference electrode generatedcorresponding to photoimage signals, is extremely safe and simple andhas a wide area of use as well as to provide an image forming materialwhich is suited for the method.

SUMMARY OF THE INVENTION

The main constitution of the image forming method of the inventioncomprises an aqueous dispersion containing a coloring material composedof a pigment and a specific electrodeposition material and a vesselthereof, an image supporting member having an electrode which cangenerate an electric image pattern and a counter electrode, and further,a jig, as an auxiliary member, for immersing the image supporting memberand the like into a vessel into which the aqueous electrodepositionmaterial dispersion is stored, and fixing them to given positions, and acontrol device for the above-described members. Regarding an imagepattern formed on the image supporting member by depositing andprecipitating an electrodeposition material by this apparatus, the imagesupporting member can be directly used as a document, and also, theimage can be transferred and fixed onto other media and used as adocument.

Namely, the image forming method according to the first aspect of thepresent invention is an image forming method wherein an aqueousdispersion containing an electrodeposition material including:

a fine particle coloring material; and

a polymer which is chemically dissolved, or deposited and precipitatedby change in pH,

is prepared in a liquid in vessel and the vessel having therein:

an image supporting member having at least:

an electrode, which can supply current or an electric field inaccordance with an image pattern,

and a surface which can support an image; and

a counter electrode which forms a pair of electrodes together with theelectrode,

and the electrodeposition material is deposited and precipitated to forman image by supporting current or an electric field in accordance withan image pattern to the image supporting member and the counterelectrode and by changing the pH value of the aqueous dispersion in thevicinity of the image supporting surface of the image supporting member,

wherein the polymer comprised in the electrodeposition material has bothhydrophobic groups and hydrophilic groups in the molecule, theproportion of the number of the hydrophobic groups to the total numberof hydrophobic groups and hydrophilic groups in the polymer is in therange of from 40% to 80%, 50% or more of the hydrophilic groups canreversibly change from hydrophilic groups to hydrophobic groups due to achange in pH value, and the acid value of the polymer is in the range offrom 30 to 400.

The image forming method according to the second aspect of the presentinvention is an image forming method wherein an aqueous dispersioncontaining an electrodeposition material including:

a coloring material; and

a polymer which is chemically dissolved, or deposited and precipitated,by a change in pH,

is prepared in a liquid in vessel and the vessel having therein:

an image supporting member having at least:

an electrode, which can supply current or an electric field inaccordance with an image pattern,

and a surface which can support an image; and

a counter electrode which forms a pair of electrodes together with theelectrode,

and the electrodeposition material is deposited and precipitated to forman image by supplying current or an electric field in accordance with animage pattern to the image supporting member and the counter electrodeand by changing the pH value of the aqueous dispersion in the vicinityof the image supporting surface of the image supporting member,

wherein the aqueous dispersion contains at least one pH regulator havinga boiling point of 150° C. or less.

Herein, the means for supplying current or electric field to theabove-described image supporting member and the counter electrodepreferably has mechanism by which a photoimage signal is converted tocurrent in accordance with an inputted photoimage signal, and generatescurrent on the surface of the image supporting member corresponding tothe photoimage signal.

In the polymer compound constituting the electrodeposition material, itis preferable that the above-described hydrophilic group part which canreversibly change from hydrophilic groups to hydrophobic groups bychange in pH has a carboxyl group or an amino group, and styrene orα-methylstyrene unit is contained in the hydrophobic group part, fromthe viewpoints of sensitivity and image supporting property.

The image forming material of the present invention is an aqueousdispersion containing a fine particle coloring material and anelectrodeposition material composed of a polymer which is chemicallydissolved or deposited and precipitated by change in pH, used in theabove-described image forming method. The electrodeposition materialcomposed of the polymer has hydrophobic groups and hydrophilic groupstogether in the molecule, the proportion of the number of thehydrophobic groups of the monomer unit constituting the polymer to thetotal number of the hydrophilic groups and the hydrophobic groups is inthe range from 40% to 80%, and 50% or more of the hydrophilic part canchange reversibly from hydrophilic groups to hydrophobic groups bychange in pH, and the electrodeposition material contains a copolymerhaving an acid value from 30 to 400.

In this image forming method, it is preferable from the viewpoint ofimage stability to perform some heating treatment on the formed image,and the heating treatment can be conducted by any method such as directapplication to an image-wise electrodeposition film, a process in whichdeposited and precipitated electrodeposition material is transferred toa recording medium by heat treatment in a transferring process,provision, or a process in which the transferred image is fixed byheating, and the like, after the process in which deposited andprecipitated electrodeposition material is transferred to a recordingmedium.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a graph showing the relation between change in pH of anaqueous coloring material liquid and the solubility property of thecoloring material.

FIG. 2 is a graph showing the relation between the molar ratio ofhydrophibic groups to (hydrophobic groups+hydrophilic groups) and thewater-resistance property of a film of an electrodeposition material.

FIG. 3 is a graph showing the water-resistance property of a film anddeposition property of an electrodeposition material.

FIG. 4 is a schematic view showing an image recording apparatus used forimage recording in Examples 1, 4, 6, 7 and 14.

FIG. 5 is a schematic view showing image recording phenomenon bydeposition of an electrodeposition material.

FIG. 6 is a schematic view showing the structure of an electrodepositedparticle in an electrodeposition liquid.

FIG. 7A to FIG. 7C are schematic views showing processes in the imageforming method of the present invention.

FIG. 8 is a schematic view showing one embodiment of the image recordingsystem of the present invention using an image recording apparatushaving an image supporting member in a shape of belt.

FIG. 9 is a schematic view showing an image recording apparatus equippedwith a laser generating apparatus used for image recording in Examples2, 8, 9 and 15.

FIG. 10 is a schematic view showing an image recording apparatusequipped with an LED printing head used for image recording in Examples3 and 16.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

The image forming method of the present invention uses an apparatus inwhich an aqueous dispersion containing a coloring material, particularlya fine particle coloring material and an electrodeposition materialcomposed of a polymer which is chemically dissolved or deposited andprecipitated by change in pH (hereinafter, suitably referred to as anaqueous coloring material electrodeposition liquid or simply anelectrodeposition liquid) is filled in a vessel which can contain liquidof an apparatus comprising in the vessel an image supporting memberhaving an electrode which can supply current or electrofield accordingto image pattern and a plane member which supports an image, togetherwith a counter electrode which is another electrode of the electrodepair.

In the second aspect of the present invention, the aqueous coloringmaterial electrodeposition liquid is allowed to contain a specific pHregulator for improving deposition sensitivity of the electrodepositionfilm.

The constituent materials of the aqueous coloring materialelectrodeposition liquid in the second aspect of the present inventionare composed mainly of a water-insoluble coloring particle, an aqueouselectrodeposition material, water and an aqueous solvent.

The constituent materials of the aqueous coloring materialelectrodeposition liquid in the first aspect of the present inventionare composed mainly of a water-insoluble coloring particle, an aqueouselectrodeposition material or colored aqueous electrodepositionmaterial, pH regulator, water and an aqueous solvent.

In any of the first and second aspects of the present invention, otheradditives such as a wetting material, aqueous polymer material,emulsifying material, latex material, various solvents, surfactant,preservative and anti-mold agent, and the like can be used provided thatthey do not harm the effect of the present invention.

As for the composition of the aqueous coloring materialelectrodeposition liquid, the concentration of solids is from 1 to 40%by weight, and preferably from 5 to 19% by weight. If the concentrationof solids is less than 1% by weight, it is difficult to obtaindispersion stability of the coloring material component, and it is alsodifficult to easily obtain a sufficient optical density of images. Onthe other hand, if the concentration of solids is more than 40% byweight, the uniformity of the liquid at the time of electrodeposition isliable to deteriorate and handling of liquid conveyance and the likebecomes complicated because the liquid exhibits thixotropy.

The content of the coloring components, in the solids of theelectrodeposition liquid, is preferably from 20% by weight to 80% byweight, preferably from 30% by weight to 80% by weight, particularlypreferably from 40% by weight to 60% by weight. A content in excess ofthis range may cause excessively high gloss of the image or may reducethe optical density of the image. On the other hand, a content less thanthis range tends to lead to disadvantages, for example,electrodeposition efficiency decreases; the image layer formation isdefective or poor and fixing strength is low; and problems occur in hue.

The resistivity of the electrodeposition liquid is 10⁶ Ω·cm or less,preferably 10⁵ Ω·cm or less, and further preferably, in the range from10³ Ω·cm to 1 Ω·cm. If the resistivity is in excess of this range, theelectrodeposition voltage becomes so high that a bubbling phenomenonaround the electrode becomes vigorous and the electrodepositionphenomenon becomes unstable and therefore the quality of the resultingfilms of the formed image tends to vary. On the other hand, when theresistivity is too low, diffusion of electric current of an image signaloccurs, and the resolution of an image decreases.

The viscosity of the electrodeposition liquid is preferably in the rangefrom 1 cps to 1000 cps, more preferably from 2 cps to 200 cps. If theviscosity is less than this range, the attendant problem is that thedroplets of the liquid are scattered because of the insufficientviscosity of the liquid. On the other hand, if the viscosity is inexcess of this range, the problem is that operation load increases andcomplicated viscosity property are exhibited in conveyance and stirringof an electrodeposition liquid and consequently efficiency decreases.

When setting the initial value of pH of the electrodeposition liquid,the pH is set to a value falling within the range from the pH value atthe start of electrodeposition −1 to the pH value at the start ofelectrodeposition +3, and preferably within the range from the pH valueat the start of electrodeposition −0.5 to the pH value at the start ofelectrodeposition +2.5, when an electrodeposition method in which anelectrodeposition material contained in the electrodeposition liquid isdeposited on an anode is used. On the other hand, the pH is set to avalue falling within the range from the pH value from the start ofelectrodeposition −3 to the pH value at the start of electrodeposition+1, and preferably within the range from the pH value at the start ofelectrodeposition −2.5 to the pH value at which pH value at the start ofelectrodeposition +0.5 when an electrodeposition method in which theelectrodeposition material is deposited on a cathode. By this setting ofthe initial value, deposition and precipitation of the electrodepositionmaterial can be conducted sharply and high electrodeposition filmformation efficiency is maintained. If the pH is set to a value which isoutside this range and which makes the deposition easier relative to thevalue at which the deposition starts, the dispersibility of theelectrodepositable liquid is so unstable that the particles of thecoloring material are deposited in non-image areas and the amountdeposited varies. Further, if the pH is set to a value which is outsidethis range and at which the deposition starts, resulting disadvantagesare, for example, that the electrodeposition film forming efficiency islow and the electrodeposition field rises; and that the properties ofthe film formed are not satisfactory.

The electrodeposition material which has an important function in theimage forming material of the present invention regarding the propertiesof the above-described preferable electrodeposition liquid has importantroles that the dispersion stability of a coloring material particle inaqueous liquid which is a main component of the electrodeposition liquidis improved, electrodeposition and adsorption phenomena are obtained,namely, rapid deposition and precipitation are attained to form anelectrodeposited film (image) by environmental electrochemical change,and water-resistance is imparted to the electrodeposited film (image).Therefore, the electrodeposition material has preferably molecularstructure containing both a group (hydrophilic group) which ishydrophilic and easily dissociated into an ion in aqueous liquid and ahydrophobic group which repels water.

The image forming action of the present invention may be explained asfollows: the ion dissociation of the hydrophilic group which has beendissociated into an ion in a polymer constituting the electrodepositionmaterial is suppressed by change in pH of the electrodeposition liquidon the surface of the image supporting member due to application ofcurrent and is allowed to exhibit hydrophobic function, thereby wholestructure of the electrodeposition material itself is hydrophobizated,the electrodeposition material containing a coloring material isinsolubilized in the aqueous liquid, and the electrodeposition materialis deposited and precipitated onto the surface of the image supportingmaterial to form an image. It is assumed that these phenomena occur bymolecular chains being spread in the electrodeposition material liquidcontract due to change in pH resulting in aggregation of the molecules,and when a coloring material fine particle is used together, depositionphenomenon of an image containing the coloring material fine particle isobserved. Thus, the polymer compound used in the electrodepositionmaterial has important roles that the dispersion stability of thecoloring particle into the aqueous liquid which is a main component ofthe electrodeposition liquid is obtained, and the electrodepositionadsorption phenomenon is caused. Therefore, the dispersion material forthe electrodeposition has preferably a molecular structure containingboth a hydrophilic group and a group which is easily dissociated into anion in aqueous liquid or a group which has the both functions. Further,it is required that the flocculation of the particle occurs by change inpH and the depositing phenomenon thereof can be observed. Theabove-described properties are necessary as functions of theelectrodeposition liquid.

Dissolution property versus change in pH of the polymer is graphicallyshown in FIG. 1, as a measure for selecting a polymer compound used inthis electrodeposition material. FIG. 1 is a graph showing the relationbetween the dissolution of the various polymers used in theelectrodeposition material and pH values of the solution. In the case ofa material having excellent balance between hydrophilic groups andhydrophobic groups in the polymer and having a hydrophilic group whichcan change to a hydrophibic group depending on conditions, depositionsteeply occurs just over a certain pH value as shown in graph A (shownby solid line), and on the other hand, in the case of a material havinga high proportion of hydrophilic groups, dissolution property isexcellent irrespective of pH value as shown in graph B (shown by brokenline). When a high proportion of hydrophobic groups is contained, thematerial is insoluble irrespective of pH value as shown in graph C(double-dashed broken line). In the case of a material in which thebalance between hydrophilic groups and hydrophobic groups is excellent,however, a hydrophilic group which can change to a hydrophobic group isnot contained or the proportion thereof is low, change indissolution/deposition is insufficient for image formation thoughdissolution property varies as shown in graph D (shown by single-dashedbroken line). These properties change also by the relation between amaterial and a solvent used. In the present invention, the case in whichdeposition steeply occurs just over a certain pH value is preferable asshown in graph A.

The electrodeposition material contains a thermoplastic resin component,and should exhibit sufficient dissolution property in an aqueous liquidin which the pH value has been regulated. Further, liquid change that acondition wherein the electrodeposition material is dissolved isconverted to a condition wherein a precipitation is formed withgenerating a supernatant occurs within the pH range of 1 in the changein the pH value of the dissolved electrodeposition liquid as shown ingraph A. For obtaining more preferred property, it is preferred that thepH range is 0.5 or less. By this range, functions can be imparted thatquick deposition of an image is enabled even against steep pH change dueto application of current, further, flocculation force of the depositedimage can be enhanced, and the re-dissolving speed into theelectrodeposition liquid is reduced. As a result, the water-resistanceof an image is also obtained. When pH range wherein a precipitation isformed from dissolved condition in the change in the pH value of theelectrodeposition liquid is larger than 1, problems in printingproperties may remain such as reduction in printing speed for obtainingsufficient image structure and deficiency in the water-resistance of animage, and the like.

For example, when a carboxyl group is used as a hydrophilic group, it isnecessary to set pH values on deposition initiation point anddissolution initiation point within acidic range, and in general, it ispreferable that the pH values on deposition initiation point anddissolution initiation point are set within the range from 5.0 to 6.9,preferably from 5.5 to 6.5. The pH values of the recording material atleast in parts in contact with the surface of the image supportingmaterial may advantageously be set to values within the above-describedrange. In practice, the deposition initiation point and the dissolutioninitiation point of the recording material can be recognized by acommercially available pH meter and visual observation using a buffersolution for the recording material.

The above-described actions and properties are required as functions ofthe electrodeposition material according to the present invention, andfor this purpose, it is necessary to obtain structures and propertiesdescribed below.

Among these electrodeposition materials, as a colorless or pale coloredpolymer compound, specifically preferable is a polymer compoundconstituted by a copolymer containing a monomer unit having ahydrophilic group which is dissociated into an ion and a minimum monomerunit having a hydrophobic group which promotes insolubilization againstan aqueous electrodeposition liquid wherein the proportion of the numberof hydrophobic groups of the minimum monomer unit of the copolymer basedon the total number of hydrophilic groups and hydrophobic groups is inthe range from 40% to 80%, more preferably from 55% to 70%, since thispolymer exhibits high electrodeposition efficiency in particular,electrodeposition property by which a film can be formed at a lowerelectrodeposition potential, and stable liquid property of theelectrodeposition liquid. The numbers of hydrophilic groups andhydrophobic groups can be calculated, for example in the case of avinyl-based polymer and the like, based on the charge ratio of monomersin conducting polymerization reaction of a polymer.

When the proportion of the number of hydrophobic groups of the monomerunit of the copolymer constituting the electrodeposition material basedon the total number of hydrophilic groups and hydrophobic groups is lessthan 40%, the electrodeposition film formed in electrodeposition isdeficient in water-resistance and film strength, and when the proportionof the number of hydrophobic groups based on the total number ofhydrophilic groups and hydrophobic groups is not less than 80%, thereare problems that dissolution property into an aqueous liquid isinsufficient, the electrodeposition liquid becomes turbid, a precipitateof the electrodeposition material is formed, the viscosity of theelectrodeposition liquid increases, and the like. Therefore, neithercase is preferable.

The relation between the water-resistance of an electrodeposition filmon which an image is formed by deposition and precipitation and theratio of the number of hydrophobic groups to the total number ofhydrophilic groups and hydrophobic groups is shown in the graph of FIG.2. Line a parallel to the abscissa of this graph indicates awater-resistant range necessary for retaining an image, and line bindicates an excellent water-resistant range. When the number ofhydrophobic groups exceeds line c parallel to the ordinate, the polymermaterial enters the range wherein the properties and conditions of thesolution are unstable due to reduction in the dissolution property ofthe polymer material, and when the number of hydrophobic groups exceedsline d, the polymer material enters the range wherein solubility is poorand measurement is impossible.

As the monomer unit containing a hydrophilic group used in thiselectrodeposition material, methacrylic acid, acrylic acid, hydroxyethylmethacrylate, acrylamide, maleic anhydride, trimellitic anhydride,phthalic anhydride, hemimellitic acid, succinic acid, adipic acid,propiolic acid, propionic acid, fumaric acid, itaconic acid and thelike, and derivatives thereof are used. In particular, methacrylic acidand acrylic acid are useful hydrophilic monomer constituting units sincethey exhibit strong action and effect in this electrodepositionphenomenon, high electrodeposition efficiency by change in pH, and highhydrophilization efficiency.

Various polymers can be used in the present invention, and vinyl-basedpolymers obtained from vinyl-based monomers, and polyester resinsobtained by polycondensation of a polyol with a polycarboxylic acid arelisted as suitable examples. The ratio of hydrophilic groups tohydrophobic groups in a polymer is as described above, and in the caseof a vinyl-based polymer, if monomers are charged so that the ratio ofthe number of hydrophobic groups of a monomer unit constituting avinyl-based polymer to the total number of hydrophobic groups andhydrophilic groups is from 40% to 80%, approximately the same ratio isgiven also in the resulting polymer. In the case of a polyester resin, apolymer having a hydroxyl group or a carboxyl group at the terminal endis obtained by the polycondensation of a hydroxyl group of a polyol witha carboxyl group of a polycarboxylic acid, and in this case, a polymerhaving a carboxylic acid at the terminal end is obtained by allowing thecharging amount of the polycarboxylic acid to exceed the amount of thepolyol. In this case, the number of hydrophobic groups and the number ofhydrophilic groups of a monomer unit used in charging are different fromthose of the resulted polymer. In the present invention, the ratio ofhydrophilic groups to hydrophobic groups in the resulting polymer isimportant.

It is preferable that 50% or more, more preferably 75% or more ofhydrophilic group part of monomer units of a copolymer constituting theelectrodeposition material is composed of hydrophilic part of a monomerunit which can change from a hydrophilic group to a hydrophobic groupreversibly. This hydrophilic group is a functional group which isdissociated into an ion in an aqueous solvent and shows hydrophilicity,and exhibits hydrophobic function by suppression of the ion dissociationdue to change in pH of the electrodeposition liquid.

Specific examples of this hydrophilic group which is dissociated into anion include a carboxyl group, amino group, sulfonic group, quaternaryammonium group, sulfuric ester group and the like, and among them, thosehaving a carboxyl group or an amino group as a hydrophilic group exhibitexcellent deposition efficiency of an image in the electrodepositionphenomenon, and show property of forming an electrodeposition filmhaving high fastness. These groups reveal high efficiency in changingreversibly from a hydrophilic group to a hydrophobic group due to changein pH, and are suitable for application to the present invention.

More particularly, when the image pattern generating part is more anodicthan the reference electrode, it is preferable that theelectrodeposition material has a carboxyl group, the carboxyl groupwhich is a hydrophilic moiety is dissociated into a negative ion groupin an aqueous liquid, simultaneously a part of this electrodepositionmaterial is bonded and adhered or associated to the surface of acoloring material particle, and the acid value of the electrodepositionmaterial is in the range from 60 to 300, and optimally, the acid valueis in the range from 90 to 150. When the image pattern generating partis more cathodic than the reference electrode, it is preferable that theelectrodeposition material has an amino group, the amino group which isa hydrophilic moiety of the electrodeposition material is dissociatedinto a positive ion group in an aqueous liquid, simultaneously a part ofthis electrodeposition material is bonded and adhered or associated tothe surface of a coloring material particle.

The electrodeposition material containing a hydrophilic group which canperform structural change shows a so-called hysteresis curve as shown inFIG. 3 by a solid line. Namely, re-dissolution is not steeply effectedand kept for a certain period of time in deposited condition in thechange in pH value, and this property is ideal from the viewpoints ofimage forming property and the stability of the resulted image. Onehaving such a re-dissolution property, namely, having a large At in thegraph of FIG. 3 in addition to the deposition property represented bygraph A shown in FIG. 1 is preferable. At is a measure for revealing thewater-resistance of the deposited electrodeposition film (image) Thepolymer compound represented by a broken line in FIG. 3 has the samestructure as that of the copolymer represented by a solid line, and hasa molecular weight of less than 4000, and has low water-resistance,therefore, it is easily re-dissolved. A material showing such are-dissolving property exhibits excellent image forming property,however, the stability of the formed image is somewhat poor, therefore,some ideas are required for maintenance of an image and conveyance ofthe image to a transfer process to a recording medium.

Not only the properties of a polymer compound but also propertiesregarding the deposition of a material relate to the formation of such ahysteresis curve. Namely, it is also known that the depositedelectrodeposition material is flocculated and a solution is expelled bya lump of the flocculated material, therefore, the amount of watercontained in an image formed by the flocculation material and a fineparticle coloring material taken into the material is controlled, andfor example, even if application of voltage is stopped and pH value ofthe solution changes again in conveying the formed image to atransferring means for conducting image transfer, the re-dissolving ofthe electrodeposition material is not initiated immediately, and thestability of the image becomes excellent.

The hydrophobic group in the structure of the electrodeposition materialhas strong affinity against an organic pigment used as a coloringmaterial, has adsorption ability for a pigment, and imparts excellentpigment dispersing function. This hydrophobic group also impartsprinting function which allows an image to be deposited quickly, inremoval of hydrophilicity of hydrophilic moiety part of theelectrodeposition material by change in pH due to application ofvoltage. Particularly, when the proportion of the number of hydrophobicgroups to the total number of hydrophilic groups and hydrophobic groupsis in the range from 40% to 80%, the effect for reducing theelectrodeposition electric potential which allows a strong film to beformed is large, and such proportion is an inevitable condition forcompleting printing process at lower electric potential usingphotoelectromotive force by input of light.

As the monomer unit containing a hydrophobic group used in thiselectrodeposition material, an alkyl group, styrene, α-methylstyrene,α-ethylstyrene, methyl methacrylate, butyl methacrylate, acrylonitrile,vinyl acetate, ethyl acrylate, butyl acrylate, lauryl methacrylate andthe like, and derivatives thereof are used. In particular, styrene andα-methylstyrene are useful hydrophilic monomer constituting units sincethey exhibit high hydrophobization efficiency, high electrodepositionefficiency and high controlling property in polymerization inproduction.

The acid value of the electrodeposition material of the type in which animage is deposited on an anode is suitably in the range from 60 to 300from the viewpoint that excellent electrodeposition property isobtained. When the acid value of the electrodeposition material is 60 orless, there occur problems that the dissolving property into an aqueousliquid is insufficient, the solid component concentration of theelectrodeposition liquid can not be raised to suitable value, the liquidbecomes turbid, a precipitate is formed, and the viscosity of the liquidincreases. When the acid value of the electrodeposition material is 300or more, the formed film has lower water-resistance, and theelectrodeposition efficiency for the amount of applied electricity islow, and the like.

The electrodeposition material according to the present inventioncontains, as a main component, a polymer compound which is obtained bycopolymerization of molecules in the above-described ratio, themolecules containing a hydrophilic group and a hydrophobic group, asdescribed above, and the kind of each hydrophilic group and hydrophobicgroup is not limited to one. The copolymer may be any of a randomcopolymer, blocked copolymer and graft copolymer.

When the average molecular weight of this copolymer is from 4,000 to30,000, an excellent electrodeposition film (deposited image) can beobtained in view of the film property of an electrodeposited film andthe adhesion strength of the film. A copolymer having an averagemolecular weight from 9,000 to 20,000 is suitable in view of a morepreferable film property of an electrodeposited film and a morepreferable adhesion strength of the film. When the average molecularweight is less than 4,000, the deposited and formed electrodepositionfilm is not uniform and the water-resistance thereof is low, therefore,the fastness of the formed image is low and there is a fear that thecopolymer is not maintained in image-wise fashion and becomes a powder.On the other hand, when the average molecular weight is higher than30,000, the dissolution property into an aqueous liquid is insufficient,there occur problems that the dissolving property into an aqueous liquidis insufficient, the solid component concentration of theelectrodeposition liquid can not be raised to suitable value, the liquidbecomes turbid, a precipitation is formed, and the viscosity of theliquid increases.

As a compound having properties in which a pigment itself is dissolvedor causes phase changes such as deposition and precipitation by changein conditions, the following compounds are exemplified. For example,Rose Bengal and Eosine which are fluoresceine-based dyes which are inthe form of reduced condition and dissolved in water at a pH of 4 ormore, and are oxidized to be in a neutralized condition and depositedand precipitated in the range of a pH of less than 4, dye materialshaving a carboxyl group of which solubility changes largely depending onthe hydrogen ion concentration (pH) even if change in structure does notoccur (specifically, inkjet dyes of which water-resistance is improvedare listed, and these are dissolved in water at a pH of 6 or more andare precipitated at a pH less than 6.), and the like are listed. Inaddition, an oxadine-based basic dye which is one of quinoneimine dyes:Cathilon Pure Blue 5GH (C. I. Basic Blue 3) and a thiazine-based basicdye: Methylene Blue (C. I. Basic Blue 9) are listed. These are in theform of oxidized condition and develop color at a pH of 10 or less, andare reduced and insolubilized to be deposited at a pH of less than 10.Further, Pro Jet Farst Yellow 2 manufactured by Zeneka Co., Ltd. whichis an acidic dye and of which dye itself has electrodeposition formingability is dissolved easily in pure water (pH 6 to 8) and exists as ananion in the aqueous solution, however, at a pH of 6 or less, it isinsolubilized and deposited.

The preferable properties of the electrodeposition material are asdescribed above, and it is preferable that the electrodepositionmaterial constituting the image formation material used in the imageforming method of the present invention has all of the above-describedproperties in good balance.

As the coloring particle used in the image forming method of the presentinvention, which having average particle diameter is in the range offrom 0.01 to 1.2 μm, preferably in the range of from 0.02 to 0.3 μm, issuitable. If the average particle diameter is smaller than theabove-mentioned range, the light screenability of the image layerdecreases to an extent that the optical image density tends to drop; theglossiness of the image is more than necessary; and safety problems tendto occur. On the other hand, if the average particle diameter is abovethe above-mentioned range, the dispersibility of the electrodepositableliquid containing the particles of the coloring material worsens to theextent that a deposited material is generated; the uniformity of theimage layer containing the particles of the coloring material is notsatisfactory; the light screenability by the particles makes the colorformability so poor that correspondence with a transmission-type imageis impossible; and the image is matted more than necessary. When theaverage particle size is 0.30 μm or less, particularly 0.20 μm or less,dispersion stability as an aqueous dispersion material is excellent andtransparency of color is high.

A dye which has no solubility or a low solubility in water or a pigmentis suitable as the coloring material in a state of fine particles.Specific examples of the pigment which can be used include inorganicpigments such as carbon black, titanium oxide, zinc white, red ironoxide, alumina white, aluminum powder, bronze powder, zinc oxide, bariumsulfate, magnesium carbonate, ultramarine blue, chromium yellow, cobaltblue, and Prussian blue; and organic pigments such as Toluidine Red,Permanent Carmine FB, Fast Yellow G, Disazo Yellow AAA, Disazo OrangePMP, Lake Red C, Brilliant Carmine 6B, Phthalocyanine Blue, IndanthronBlue, Quinacridone Red, Dioxazine Violet, Victoria Pure Blue, AlkaliBlue toner, aniline black, Permanent Red 2B, Barium Lithol Red,Quinacridone Magenta, Naphthol Red HF4B, Phthalocyanine Green, andBenzimidazolone Red, oil-soluble dyes such as Victoria Blue 4R Base,Nigrosin, Nigrosin Base, C.I. Solvent Yellow 19, C.I. Solvent Orange 45,and C.I. Solvent Red 8. Further, a disperse dye, a dyed lake pigment, ora resin powder incorporated with a colorant can be listed for obtainingsuitable properties.

These coloring material fine particles may be used as coloringcomponents of a colorless or pale-colored electrodeposition material, orcan be used together with a colored electrodeposition material tocontrol the hue of the electrodeposited film.

These electrodeposition materials showed excellent properties indispersion stability and film property of an electrodeposited film byaddition of a surfactant having an ionic substituent, a water-solublepolymer and a polymer having a low polymerization degree.

Examples of water-soluble polymers and polymers having a low degree ofpolymerization which perform preferable effect as an additive includealkylalkylene oxide carboxylate, alkyloxide carboxylate, alginicacid-modified carboxylate, carboxy-modified methylcellulose, polyacrylicacid-modified carboxylate, acrylic acid-modified carboxylate,polyethylene oxide-modified carboxylate, epoxy-modified carboxylate,polyethanolamine-modified methylcellulose, amine-modified alginate, andamine-modified polyacrylic acid. These are effective as dispersionmaterials.

The pH regulator used in the present invention has main actions that thepH value of a coloring material dispersed electrodeposition liquid iscontrolled to a value at which an electrodeposition material is easilydeposited and precipitated, a dispersion material is allowed to actefficiently to secure the dispersion stability of a coloring material,solubility into water and a main solvent is easily imparted to anelectrodeposition dispersion material, and the like. After an image isformed by an electrodeposition film, it is preferable to remove the pHregulator quickly since the pH regulator has effect to reduce thewater-resistance of the electrodeposited image.

In the image forming method of the present invention, a single kind ofpH regulator may be used in an aqueous dispersion, or a plurality of pHregulators may be contained. In any case, at least one kind of pHregulator is utilized to control pH toward a pH range wherein theelectrodeposition material is easily dissolved in the above-describedaqueous dispersion, and it is required that the boiling point of the pHregulator having this action is 150° C. or less. Namely, the reason forthis is that when an electrodeposition film is formed in an imagesupporting member, and this image formed by electrodeposition is allowedto stand with containing the pH regulator, the pH regulator would(re-)dissolve the image formed by electrodeposition and the formed imageis degraded.

In this case, when a pH regulator having a boiling point of 150° C. orless is used, this pH regulator is quickly and easily removed when it isallowed to stand in atmosphere or heated in an image transferringprocess, image fixing process and the like. By this, the pH regulator inan electrodeposition image is removed quickly with a lapse of time byevaporation when allowed to stand naturally, deterioration of an imageis prevented, and water-resistance and fastness are improved. Further,by conducting heating treatment after deposition of an electrodepositionfilm (image formation), the pH regulator is removed more efficiently ina shorter period of time, therefore, time during which the pH regulatorexists in the electrodeposition film steeply reduces, deterioration ofan image is prevented, water-resistance of an image is extremelyimproved, and the fastness of an image is largely enhanced. Thus,remarkable effect is obtained by removing the pH regulator in the pHrange wherein re-dissolving is promoted.

Because of the above-described reasons, when an aqueous dispersioncontains a plurality of pH regulators, only pH regulator for controllingthe pH range where an electrodeposition material is dissolved mayadvantageously have a boiling point of 150° C. or less, but the pHregulator for controlling the pH range where an electrodepositionmaterial is deposited and precipitated is not necessarily required tohave a boiling point of 150° C. or less.

For heating treatment of the formed image, a method in which anelectrodeposition film formed on an image supporting member is directlyheated, a method in which an electrodeposition material is transferredto a recording medium by heat treatment, a method in which after anelectrodeposition material is transferred to a recording medium, animage formed by the transfer is heated, and the like can be listed.However, the heating method and time during which heating process isperformed are not particularly restricted when the removal of the pHregulator can be conducted by appropriate heating treatment. Alsoregarding the heating method, a contact heating using a roller or platecontaining a heater, and non-contact heating using hot air, infrared rayor the like may be permissible, and in the case of the contact heating,a pressure may be applied together, or only heating may be effected.

As the pH regulator which can be suitably used, any regulator can beused if it has the above-described preferable boiling point (not morethan 150° C.). However, pH regulators having a boiling point of about 30to 120° C. are preferable in view of the effect. When the boiling pointis over 150° C., there is a fear that the pH regulator remains in theelectrodeposition film and the stability of the film is reduced, andwhen the boiling point is less than 30° C., the stability in theelectrodeposition liquid is insufficient, pH in the electrodepositionliquid easily changes, and uniform and stable image formation isdifficult.

As the pH regulator which can be suitably used, ammonia (boiling point:not more than −33.4° C., hereinafter shown in brackets),methylaminoethanol (135° C.), dimethylaminoethanol (134° C.),ethylaminoethoanol, ethylenediamine (116.5° C.) propylenediamine (119.3°C.), methylamine (−6.3° C.), dimethylamine (−93.0° C.), trimethylamine(3.4° C., 755 mmHg), monoethylamine (16.6° C.), diethylamine (55.5° C.),triethylamine (89.4° C., 760 mmHg), propylamine (49.7° C.),dipropylamine (109.2° C.), butylamine (78° C.), pentylamine (104.5° C.),hydrogen chloride (−85° C.), formic acid (101° C.), acetic acid (118°C.), hydrochloric acid (−85° C.) and the like are listed. The measuringmethod of boiling point, known methods can be applied, and in the caseof a simple body, values described in literatures such as ChemicalHandbook and the like can be referred.

As the aqueous solvent which can be used together with theabove-described electrodeposition material and coloring particle, water;alcohols such as methanol, ethanol, butanol, and isopropyl alcohol;ketones such as acetone and methyl ethyl ketone; amines such as ethanolamine, dimethyl amine, and triethanol amine; and acids such as aceticacid, sulfuric acid, hydrochloric acid, phosphoric acid, oxalic acid,and phthalic acid can be used alone or in combination of two or more,and in particular, a mixed solvent whose main component is water is veryuseful from the viewpoints of safety, stability, and cost.

It is preferable to compound a water-soluble solvent as a wettingmaterial for preventing modification of an electrodeposition liquid dueto evaporation of an aqueous solvent component. As this water-solublesolvent, a liquid which is highly hydrophilic and has an azeotropicpoint with water, a high boiling point and a low vapor pressure may beadvantageous. Preferably, the liquid is a solvent which has a highpolarity and which has a boiling point of 150° C. or higher and asaturated vapor pressure of 100 mmHg or lower at room temperature underatmospheric pressure, and preferably a boiling point of 150° C. orhigher and a saturated vapor pressure of 60 mmHg or lower underatmospheric pressure. Outside this range, evaporation of theelectrodeposition liquid is high, the life of the dispersion is shorterand a stable deposition performance cannot be obtained because theproperties of the liquid largely change. The composition ratio ispreferably in the range of from 0.5 to 70% by weight, and morepreferably in the range of from 5 to 30% by weight. Specific and typicalexamples thereof include ethylene glycol, diethylene glycol,polyethylene glycol, glycerin, diacetone alcohol, methyl cellosolve,ethyl cellosolve, butyl cellosolve, and ethylene glycol diacetate.

The addition of a polymeric additive and an emulsion imparts a stablefilm forming property at the time of electrodeposition and is veryeffective in improving the film properties of the electrodepositionfilm, in improving the fastness of the electrodeposition image and incontrolling the electrical resistance of the film. The amount to beadded is preferably in the range of from 0.2 to 50% by weight, and morepreferably in the range of from 1 to 15% by weight, based on solids.

Typical examples of the polymeric additive include gelatin, gum arabic,pectin, casein, starch, microcrystalline cellulose, alginates, polyvinylalcohol, vinyl acetate copolymers, polyacrylic acid copolymers, andderivatives of methyl cellulose.

Typical examples of the emulsion include polyvinyl acetate emulsions,vinyl acetate copolymer emulsions, acrylate copolymer emulsions, andsynthetic rubber latex.

Besides these, it is possible to add a preservative, an anti-mold agent,a very small amount of a surfactant, an agent which adjusts theviscosity of the liquid, and the like. It is preferable to add thepreservative and the anti-mold agent to the aqueous liquid from theviewpoint of the stability of the liquid, because the aqueous liquid isliable to deteriorate due to the growth of microorganisms and moldssince an aqueous liquid is used as the dispersion medium in the presentinvention.

Preferable image forming conditions in the image forming method of thepresent invention and an apparatus which is suitably used in the methodare illustrated below.

For voltage difference to be applied between an electrode and an imagesupporting member in the image forming (electrodeposition) process inthe method of the present invention, a direct current power sourcehaving a value less than ±9 V is often used. In order to reproduce eachpixcel sharply of an image, signals can be inputted using direct currentpulse at a short time interval and the short pulse in combination. Asthe voltage difference to be applied, a direct power source having avalue of 3 V or less is more preferably used, and when film property isimportant, direct power source having a value of 2.5 V or less is used.When a voltage difference of 9 V or more is applied, generation ofbubbles due to electrolysis of a solution from the surface of anelectrode in the liquid is intense, electric field distribution on thesurface of the electrode becomes ununiform, the film property of a filmitself becomes ununiform, the surface of the film becomes uneven due todefoaming phenomenon of bubbles, and intended reproduction of an imagehaving fine pattern is difficult.

There is electrodeposition coating as a technology resembling the imageforming process of the present invention, and in general, in thiselectrodeposition coating, a voltage of 50 V or more is applied. Thereason for this is that if voltage applied is low, the resistance of theformed electrodeposition film may sometimes be high, theelectrodeposition film forming speed lowers largely with progress of theelectrodeposition film formation and required film thickness (generally,30 μm or more) can not be obtained, therefore, high voltage is appliedand intense foaming phenomenon is allowed to occur by electrolysis foravoiding the above-described defects, stirring near the surface of anelectrode is conducted and the surface of the electrode is brought intocontact with new electrodeposition liquid by utilizing the phenomenon,to obtain a film thickness required as the electrodeposition coating.

The aim of the present invention is reproduction of an image having highimage quality, specifically, reproduction of a fine image (400 dpi ormore) pattern having a film thickness level of 2 μm or less, therefore,the bubbling phenomenon due to electrolysis of an electrodepositionliquid is required to be suppressed, and if any, it should be suppressedto a level which does not exert influence on the reproduction of a fineimage pattern. By this, the voltage difference applied becomes a directcurrent of 5 V or less, in more fine image (800 dpi or more) printing,preferably 3 V or less, and when image quality is regarded important,2.5 V or less. Further, as the voltage applying means, triple-electrodemethod may sometimes be used in which the stability of voltage is takeninto consideration. Further, since image forming can be conducted byapplication of such small voltage difference, a mechanism which convertsan inputted photo-image signal into current can be used in the imageforming process of the present invention.

Namely, photoelectromotive force is usually 1 V or less, and forexample, in a widely used apparatus using a silicon-based material, fromabout 0.6 to 0.7 V, and when it is considered that bias voltage is fromabout 2 to 5, it can be understood that the image forming method of thepresent invention can be suitably used for input of a photo imagesignal.

In the case of writing with light, structure is formed in which an imagesupporting member is composed of at least a flat electrode layer andphotoconductive material layer, and current flows on the surface of theimage supporting member in the area irradiated with light andelectrodeposition phenomenon of a coloring material particle occurs.

Then, an image recording apparatus which can be suitably used in theimage recording method of the present invention will be described. FIG.4 is a schematic view showing the image recording apparatus of thepresent invention used in Example 1 and Example 14 described later. Inthis image recording apparatus, an image supporting member 3 composed ofa plane member equipped with a work electrode into which an image signalcan be inputted from the rear surface is placed in an electrodepositionliquid bath 1 filled with an aqueous coloring material liquid 1 forelectrodeposition so that the rear surface is out of the liquid bath,and a counter electrode 5, and control electrode 6 utilizing a saltbridge is also place in the same bath. This image supporting member 3 ismade by a lamination structure in which a transparent conductive layerof ITO is given on a 4 mm plate glass substrate and two layers of anorganic photoconductor are given on the transparent layer, and the ITOconductive layer is a work electrode, and the surface of the organicphotoconductive layer has no unevenness and is smooth. Each electrode isconnected to a potentiostat power source 4, and voltage is appliedbetween the rear surface of the image supporting member 3 and thecounter electrode 5 by the potentiostat power source 4 with inputting animage to photoimage input part on the rear surface of the imagesupporting member 3 and an electrodeposition material in anelectrodeposition liquid is allowed to be deposited together with acoloring material particle onto the surface of the image supportingmember 3 to form an image. The image herein recorded can also betransferred and fixed to a transfer material such as plain paper orplastic film, if necessary.

This image recording method will be described in detail. FIG. 5 is aschematic view showing image recording phenomenon by deposition of anelectrodeposition material. When voltage is applied from a directcurrent power source 8 to a pseudo current supply electrode 7 placedimagewisely on the image supporting member 3, pH of an electrodepositionliquid 1 near the electrode 7 changes, and electrodeposition material 9containing a coloring particle dissolved and dispersed into theelectrodeposition liquid 1 is deposited on the surface of the imagesupporting member 3, and a polymer compound containing the coloringmaterial deposited in the form of an image is adhered to record an image10. FIG. 6 is a schematic view showing the structure of theelectrodeposition particle in the electrodeposition liquid. In theelectrodeposition liquid, it is assumed that polymer compound 25constituting the electrodeposition material exists near the surface of acoloring particle 24 so as to cover the particle, and a part thereofexists as free ions 26 in the electrodeposition material.

Next, process in which thus recorded image is transferred and fixed toanother recording medium will be described. FIG. 7(A) is a schematicview showing the above-described image recording process. The formedimage 10 is supported on the recording material deposited on the surfaceof the image supporting member 3. FIG. 7(B) is a-schematic view showingan image transferring process. Plain paper 11 which is a transfermaterial is laminated on the image supporting member 3 taken out of theaqueous electrodeposition liquid, pressed by a transfer roller 12, andfurther, preferably heated and pressed, to allow the image to betransferred and fixed on the plain paper 11. FIG. 7(C) shows the image10 transferred and fixed on the plain paper 11, and thus recording of animage onto plain paper (transfer material) 11 is completed.

As to the image supporting member to be used in the present invention,the requirements are that the surface on which images are formed ishighly smooth and free from unevenness so as to obtain good printingperformance and that the surface energy is low so as to obtain goodtransfer performance. In addition, these properties are also importantfrom the viewpoint of the prevention of the image retention in the casewhere the image supporting member is used repeatedly to form a differentimage.

More specifically, in order to obtain good transferability, the surfaceroughness (Ra) of the surface of the image supporting member is in therange of from 0.01 to 1.5 μm, and preferably in the range of from 0.06to 0.5 μm. In addition, in order to obtain good transferability, thecritical surface tension of the surface of the image supporting memberis in the range of from 35 dyne/cm or less, and preferably in the rangeof from 20 to 29 dyne/cm.

By this viewpoint, it is necessary to form a low surface energy layer onthe surface of the image supporting member, and examples of the materialproviding such a surface layer include a fluororesin, a fluororubber(FEP), a dimethylsiloxane resin, a silicone rubber, wax-based materialsand the like, and a composite material comprising any of these materialsand an electrically conductive powder so as to control the electricalresistance of the layer itself.

The image supporting member having a surface which has high smoothnessas described above, and has low surface energy can provide excellentprinting property. Particularly, this property will be an importantproperty if the image supporting member is used repeatedly. Theseproperties improve the physical cleanability of the image on the imagesupporting member. As a result, even if the image is different for everyrecording, it is possible to establish a printing cycle which is freefrom the hysteresis of the image information of the preceding recording.

In the image forming process, it is preferable to conduct stirring inthe liquid bath for maintaining uniformity of the liquid property of thebath of the electrodeposition liquid, in view of ability of formation animage (electrodeposition film) having uniformity. When the stirring istoo strong, film formation may be delayed and liquid scattering mayoccur, therefore, it is necessary to select suitable stirring conditionswith considering the conditions of the liquid.

A more uniform excellent film property can be obtained by controllingthe liquid temperature. Since this phenomenon itself is affected by theliquid temperature, when reproduction of high quality image is intended,it is necessary to provide a liquid temperature control systemparticularly having high accuracy.

The image formed on the flat surface of the image supporting member inthe image forming process can be transferred to another recordingmedium. In the transfer process of an image, the formed image(electrodeposition film) is transferred to a transfer medium such asplain paper and the like from the image supporting member usingelectrostatic force, pressure, adhesiveness, or the like.

Particularly, in the image transfer process, by conducting imagetransfer under conditions containing a suitable amount of the liquidcomponent of the electrodeposition liquid in forming a film, thetransferred image material exhibits property having viscous property,and only pressure in the transferring process of an image can generateviscous deformation of the image and transfer is made possible. By this,image forming process can also be made wherein the whole system is morecompact and unnecessary energy is not consumed.

If the image supporting member is in a shape of a belt, the recording ofimage can be performed effectively because the recording, transfer tothe transfer-receiving medium and fixing of an image can be performedcontinuously.

When preparing such a belt-shaped image supporting member, the materialsfor the substrate are, for example, polymers, such as polyimide resinsand modified compounds thereof, polyaramide resins and modifiedcompounds thereof, and silicone resins and modified compounds thereof aswell as materials composed mainly of these polymers. If the imagesupporting member is in the shape of a belt, the coloring materialadhering to the surface can be effectively removed by bending the beltat an acute angle, which makes it possible to improve the physicalcleanability of the image on the image supporting member. As a result,even if the image is different for every recording, it is possible toestablish a printing cycle which is free from the hysteresis of theimage information of the preceding recording.

FIG. 8 is a schematic diagram illustrating one embodiment of the imagerecording apparatus system according to the present invention. Since theimage supporting member 3 is in the shape of a belt, an image 10, whichis recordedby receiving an optical signal in the aqueous coloringmaterial liquid 1, is conveyed forward while being adhered to thesurface of the belt-shaped image supporting member 3. In thetransferring section, the image 10 is transferred to a paper 11 suppliedfrom a paper roll 19 when the image 10 passes through a gap betweenpressing and heating rolls 12. The colorant remaining on the imagesupporting member 3 is removed with a cleaning brush 20 and isaccumulated in a bowl 21 for cleaning waste. The image supporting member3, after being cleaned by the cleaning brush 20, is again used for imagerecording.

When the image supporting member is made in the form of a belt andcontinuously used as described above, it is preferable to remove thecoloring material, electrodeposition material and the like remaining onthe surface of the plain member after completion of the image formingprocess and image transferring process and before the image formingprocess is effected again. For removing the image forming materialremaining on the surface of the plain member of the image supportingmember, known cleaning methods such as a blade-cleaning method,fur-brushing method, elastic roller method, cleaning web method, liquidwashing method and the like can be applied.

The image forming method is a recording method in which an imagesupporting member which generates current corresponding to a photoimagesignal is placed in a liquid containing a coloring particle in anaqueous medium, and electrodeposition phenomenon is allowed to occurcorresponding to the image current and an image containing ioniccoloring material particle group is formed on the surface of the imagesupporting member, and an image forming method also containing a postprocess in which the recorded image is transferred to a receivingmedium. In particular, it is an image forming method in which thetransferring process is conducted when an image adhered onto the surfaceof the image supporting member contains the liquid component of theelectrodeposition liquid, and since an image having photoimage qualityhaving high resolution can be formed by applying a low voltage, theprocess has wide application.

EXAMPLES

The following examples further illustrate the present invention indetail but do not limit the present invention.

Example 1

90 parts by weight of 20% by weight aqueous alkali solution of astyrene-acrylic acid copolymer (molecular weight: 13,000, hydrophobicgroup/(hydrophilic group+hydrophobic group) molar ratio: 65%, acidvalue:150), 11 parts by weight of carbon black powder (having an averageparticle diameter of 0.08 μm), 15 parts by weight of diethylene glycol,7 parts by weight of isopropanol, and 15 parts by weight of distilledwater were mixed, and moderately stirred for 1 hour by means of apropeller to sufficiently wet the carbon black powder with the liquidand thus to prepare a dispersion containing roughly dispersed carbonblack powder. This dispersion was then subjected to an intensive,forced-dispersing treatment using a homogenizer for 6 minutes to preparea base dispersion. Into this base dispersion was dropwise added a dilutesolution containing 60 parts by weight of distilled water, 10 parts byweight of glycerin, and 0.8 parts by weight of an anti-mold agent((Proxycel XL-2 manufactured by ICI Inc.) while the liquid was stirredwith a propeller. In this way, a dispersion containing fine particles ofa coloring material for use in electrodeposition was prepared. The pH ofthis liquid was set to 7.9 by adjusting pH using an aqueous solution ofphosphoric acid and an aqueous solution of sodium hydroxide. The pH atwhich the fine particles of the coloring material started depositingfrom the liquid was 6.2. The pH at which precipitation leaving acomplete supernatant occurred was 5.7.

The resistivity of the liquid was 5×10² Ω·cm.

In the image recording apparatus as illustrated in FIG. 4, this aqueouscoloring material liquid was used to record an image. As shown in FIG.4, in an electrodeposition bath 2 filled with the electrodepositionliquid 1 was disposed an image supporting member 3, whose rear surfacewas fitted with a working electrode so that an image signal could beinputted, in such a manner that the rear surface was exposed to theoutside of the bath. Further, in the bath 2 were disposed a counterelectrode 5 and a controlling electrode 6 utilizing a salt bridge. Theimage supporting member 3 had a multilayered structure comprising a 3 mmthick plate glass substrate having a transparent electrically conductivelayer of ITO formed thereon, and the transparent electrically conductivelayer was covered with two organic photoconductive layers. Theelectrically conductive layer of ITO functioned as a working electrodeand the surface of the organic photoconductive layer was smooth withoutunevenness. The respective electrodes were connected to a potentiostatpower source. An image signal was inputted into an optical imageinputting section on the rear surface of the image supporting memberwhile a DC voltage of 2.7 V was applied between the working electrodeand the counter electrode for 5 seconds by means of the potentiostatpower source.

Next, the image supporting member which had completed this imageformation procedure was withdrawn from the liquid, and it was confirmedthat a high quality image having an optical image density of 1.43 wasformed on the surface of the image supporting member.

Example 2

120 parts by weight of 20% by weight aqueous alkali solution of aa-styrene-methacrylic acid copolymer (molecular weight: 17,000,hydrophobic group/(hydrophilic group+hydrophobic group) molar ratio:70%, acidvalue: 160), 20 parts by weight of carbon black powder (havingan average particle diameter of 0.07 μm), 10 parts by weight ofpolyethylene glycol, 10 parts by weight of isopropanol, and 20 parts byweight of distilled water were mixed, and moderately stirred for 1 hourby means of a propeller to sufficiently wet the carbon black powder withthe liquid and thus to prepare a dispersion containing roughly dispersedcarbon black powder. This dispersion was then subjected to a dispersingtreatment using a ball mill for 35 hours to prepare a base dispersion.Into this base dispersion was dropwisely added a diluted mixture of adilute solution containing 100 parts by weight of distilled water, 20parts by weight of glycerin, and 0.5 parts by weight of an anti-moldagent ((Proxycel XL-2 manufactured by ICI Inc.) while the mixture wasstirred with a propeller. In this way, a dispersion containing fineparticles of a coloring material for use in electrodeposition wasprepared. The pH of this liquid was set to 8.1 by adjusting pH the usingan aqueous solution of phosphoric acid and an aqueous solution ofammonia. The pH at which the fine particles of the coloring materialstarted depositing from the liquid was 6.3. The pH at whichprecipitation leaving a clear supernatant occurred was 5.9. Theresistivity of the liquid was 2×10² Ω·cm.

The image recording apparatus as illustrated in FIG. 9 was used, and, inan electrodeposition bath 2 filled with the electrodeposition liquid 1was disposed an image supporting member 3, whose rear surf ace wasfitted with a working electrode so that an image signal could beinputted, in such a manner that the rear surface was exposed to theoutside of the bath. Further, in the bath 2 were disposed a counterelectrode 5 and a controlling electrode 6 utilizing a salt bridge. Theimage supporting member 3 had a multilayered structure comprising a 2 mmthick plate quartz substrate having a transparent electricallyconductive layer of ITO formed thereon, and the transparent electricallyconductive layer was covered with two organic photoconductive layers.The electrically conductive layer of ITO functioned as a workingelectrode and the surface of the organic photoconductive layer wassmooth. The respective electrodes were connected to a potentiostat powersource. An image signal was inputted into an optical image inputtingsection on the rear surface of the image supporting member by a He—Nelaser ray 23 which was radiated from a laser source 22, while a DC pulsevoltage of 2.9 V (pulse width 3 ms/pulse cycle 4 ms) was applied betweenthe working electrode and the counter electrode by means of thepotentiostat power source 4.

Next, the image supporting member which had completed this imageformation procedure was withdrawn from the liquid, and it was confirmedthat a high quality image having an optical image density of 1.48 wasformed on the surface of the image supporting member.

Example 3

150 parts by weight of 20% by weight aqueous alkali solution of astyrene-a-styrene-acrylic acid copolymer (molecular weight: 11,000,hydrophobic group/(hydrophilic group+hydrophobic group) molar ratio:72%, acid value: 140), 10 parts by weight of phthalocyanine powder(having an average particle diameter of 0.2 μm), 6 parts by weight of awater-soluble acrylic resin, and 10 parts by weight of isopropanol weremixed, and moderately stirred for 0.5 hours by means of a propeller tosufficiently wet the carbon black powder with the liquid and thus toprepare a dispersion containing roughly dispersed carbon black powder.This dispersion was then subjected to a dispersing treatment using ahomogenizer for 10 hours to prepare a base dispersion. Into this basedispersion was dropwisely added a diluted mixture of a dilute solutioncontaining 100 parts by weight of distilled water, 20 parts by weight ofdiethylene glycol, and 0.5 parts by weight of an anti-mold agent((Proxycel XL-2 manufactured by ICI Inc.) while the mixture was stirredwith a propeller. In this way, a dispersion containing fine particles ofa coloring material for use in electrodeposition was prepared. The pH ofthis liquid was set to 7.7 by adjusting pH the using an aqueous solutionof phosphoric acid and an aqueous solution of lithium hydroxide. The pHat which the fine particles of the coloring material started depositingfrom the liquid was 6.3. The pH at which precipitation leaving a clearsupernatant occurred was 5.9. The resistivity of the liquid was 9×10²Ω·cm.

The image recording apparatus as illustrated in FIG. 10 was used, and,in an electrodeposition bath 2 filled with the electrodeposition liquid1 was disposed an image supporting member 3 into which an image signalcould be inputted, in such a manner that the rear surface was exposed tothe outside of the bath. Further, in the bath 2 were disposed a counterelectrode 5 and a controlling electrode 6 utilizing a salt bridge. Theimage supporting member 3 had a 5 mm thick electrically conductive layerof which current dispersion had been suppressed and the surface incontact with liquid of the electrically conductive layer was smooth. Therespective electrodes were connected to a control power source. An imagesignal was inputted into an image inputting section using a needleelectrode image inputting printing head 28 of 600 DPI, while a DC pulsevoltage of 3.1 V (pulse width 2 ms/pulse cycle 3 ms) was applied betweenthe needle electrode and the counter electrode in synchronization withthe scanning speed of the printing head 28.

Next, the image supporting member which had completed this imageformation procedure was withdrawn from the liquid, and it was confirmedthat a cyan-colored high quality image having an optical image densityof 1.53 was formed on the surface of the image supporting member.Further, printing was conducted, while a DC pulse voltage of 2.3 V wasapplied between the needle electrode and the counter electrode, and itwas confirmed that a cyan-colored high quality image having an opticalimage density of 1.15 was formed on the surface of the image supportingmember.

Example 4

220 parts by weight of 20% by weight aqueous alkali solution of astyrene-maleic anhydride copolymer (molecular weight: 8,000, hydrophobicgroup/(hydrophilic group+hydrophobic group) molar ratio: 62%, acidvalue:190), 20 parts by weight of carbon black powder (having an averageparticle diameter of 0.07 μm), 10 parts by weight of polyethyleneglycol, 3 parts by weight of a water-souble acrylic resin, 10 parts byweight of isopropanol, and 50 parts by weight of distilled water weremixed, and moderately stirred for 3 hours by means of a propeller tosufficiently wet the carbon black powder with the liquid and thus toprepare a dispersion containing roughly dispersed carbon black powder.This dispersion was then subjected to a dispersing treatment using aball mill for 24 hours to prepare a base dispersion. Into this basedispersion was dropwisely added a dilute solution containing 80 parts byweight of distilled water, 10 parts by weight of glycerin, 4 parts byweight of pyrrole and 0.5 parts by weight of an anti-mold agent((Proxycel XL-2 manufactured by ICI Inc.) while the liquid was stirredwith a propeller. In this way, a dispersion containing fine particles ofa coloring material for use in electrodeposition was prepared. The pH ofthis liquid was set to 7.8 by adjusting pH the using an aqueous solutionof phosphoric acid and an aqueous solution of ammonia. The pH at whichthe fine particles of the coloring material started depositing from theliquid was 5.9. The pH at which precipitation leaving a clearsupernatant occurred was 5.4.

The resistivity of the liquid was 1×10² Ω·cm.

The same apparatus as in Example 1 as illustrated in FIG. 4 was used,and, in an electrodeposition bath 2 filled with the electrodepositionliquid 1 was disposed an image supporting member 3, whose rear surfacewas fitted with a working electrode so that an image signal could beinputted, in such a manner that the rear surface was exposed to theoutside of the bath. Further, in the bath 2 were disposed a counterelectrode 5 and a controlling electrode 6 utilizing a salt bridge. Theimage supporting member 3 had a multilayered structure comprising a 2 mmthick plate quartz substrate having a transparent electricallyconductive layer of ITO formed thereon, and the transparent electricallyconductive layer was covered with two organic photoconductive layers.The electrically conductive layer of ITO functioned as a workingelectrode and the surface of the organic photoconductive layer wassmooth. The respective electrodes were connected to a potentiostat powersource. An image signal was inputted into an optical image inputtingsection on the rear surface of the image supporting member by a He—Nelaser ray 23, while a DC pulse voltage of 2.2 V was applied between theworking electrode and the counter electrode by means of the potentiostatpower source 4.

Next, the image supporting member which had completed this imageformation procedure was withdrawn from the liquid, and it was confirmedthat a high quality image having an optical image density of 1.26 wasformed on the surface of the image supporting member.

Example 5

According to the same manner as in Example 1, a dispersion forelectrodeposition was prepared, the image forming process was conducted,the image supporting member on which surface an image had been formedwas taken out from the electrodeposition bath, and plain paper wasplaced on the surface of the image supporting member on which an imagecontaining the coloring material particle had been formed. Coronadischarge of +6 KV was effected from this paper, then, the plain paperand the image supporting member were sandwiched between a pair of rubberrollers at a linear load of 500 g/cm by applying pressure and conveyedby the rotation of the rollers. Directly after the application ofpressure, the plain paper was peeled from the image supporting member,and a transferred image having an optical image density of 1.36 wasformed on the plain paper.

Example 6

180 parts by weight of 20% by weight aqueous alkali solution of astyrene-acrylate-acrylic acid copolymer (molecular weight: 16,000,hydrophobic group/(hydrophilic group+hydrophobic group) molar ratio:2.0, acid value: 180), 15 parts by weight of carbon black powder (havingan average particle diameter of 0.07 μm), 15 parts by weight ofglycerin, 7 parts by weight of isopropanol, and 55 parts by weight ofdistilled water were mixed, and moderately stirred for 1 hour by meansof a propeller to sufficiently wet the carbon black powder with theliquid and thus to prepare a dispersion containing roughly dispersedcarbon black powder. This dispersion was then subjected to an intensive,forced-dispersing treatment using a homogenizer for 3 minutes to preparea base dispersion. Into this base dispersion was dropwisely added adilute solution containing 100 parts by weight of distilled water, 80parts by weight of vinyl acetate emulsion aqueous solution and 0.6 partsby weight of an anti-mold agent ((Proxycel XL-2 manufacturedby ICI Inc.)while the liquid was stirred with a propeller. In this way, a dispersioncontaining fine particles of a coloring material for use inelectrodeposition was prepared. The pH of this liquid was set to 7.8 byadjusting pH using an aqueous solution of phosphoric acid and an aqueoussolution of sodium hydroxide. The pH at which the fine particles of thecoloring material started depositing from the liquid was 5.9. The pH atwhich precipitation leaving a clear supernatant occurred was 5.6. Theresistivity of the liquid was 5×10² Ω·cm.

Then, as illustrated in FIG. 4, in an electrodeposition bath 2 filledwith the electrodeposition liquid 1 was disposed an image supportingmember 3, whose rear surface was fitted with a working electrode so thatan image signal could be inputted, in such a manner that the rearsurface was exposed to the outside of the bath. Further, in the bath 2were disposed a counter electrode 5 and a controlling electrode 6utilizing a salt bridge. The image supporting member 3 had amultilayered structure comprising a 4 mm thick blue glass platesubstrate having a transparent electrically conductive layer of ITOformed thereon, and the transparent electrically conductive layer wascovered with two organic photoconductive layers. The electricallyconductive layer of ITO functioned as a working electrode and thesurface of the organic photoconductive layer was smooth. The respectiveelectrodes were connected to a potentiostat power source. An imagesignal was inputted into an optical image inputting section on the rearsurface of the image supporting member, while a DC pulse voltage of 2.6V was applied between the working electrode and the counter electrodefor 9 seconds by means of the potentiostat power source 4.

Next, the image supporting member which had completed this imageformation procedure was withdrawn from the liquid, and it was confirmedthat a high quality image having an optical image density of 1.48 wasformed on the surface of the image supporting member. Then, a rubbereraser scrubbing fixing test was conducted, and change in opticaldensity of the printing sample was 0.2. On the other hand, the samefixing test was conducted on the printing sample in Example 1, andchange in optical density of the printing sample was 0.5. By this, itwas confirmed that fixing property was improved by addition of theemulsion aqueous solution.

Example 7

90 parts by weight of 20% by weight aqueous alkali solution of astyrene-acrylic acid copolymer (molecular weight: 13,000, hydrophobicgroup/(hydrophilic group+hydrophobic group) molar ratio: 68%, acidvalue:150), 11 parts by weight of carbon black powder (having an averageparticle diameter of 0.08 μm), 7 parts by weight of isopropanol, and 15parts by weight of distilled water were mixed, and moderately stirredfor 1 hour by means of a propeller to sufficiently wet the carbon blackpowder with the liquid and thus to prepare a dispersion containingroughly dispersed carbon black powder. This dispersion was thensubjected to an intensive, forced-dispersing treatment using ahomogenizer for 3 minutes to prepare a base dispersion. Into this basedispersion was dropwisely added a dilute solution containing 140 partsby weight of distilled water, and 0.3 parts by weight of ananti-moldagent ((Proxycel XL-2 manufactured by ICI Inc.) while theliquid was stirred with a propeller. In this way, a dispersioncontaining fine particles of a coloring material for use inelectrodeposition was prepared.

Then, the same apparatus as in Example as illustrated in FIG. 4 wasused, and in an electrodeposition bath 2 filled with theelectrodeposition liquid 1 was disposed an image supporting member 3,whose rear surface was fitted with a working electrode so that an imagesignal could be inputted, in such a manner that the rear surface wasexposed to the outside of the bath. Further, in the bath 2 were disposeda counter electrode 5 and a controlling electrode 6 utilizing a saltbridge. An image signal was inputted into an optical image inputtingsection on the rear surface of the image supporting member, while a DCpulse voltage of 2.5 V was applied between the working electrode and thecounter electrode for 7 seconds by means of the potentiostat powersource 4.

Next, the image supporting member which had completed this imageformation procedure was withdrawn from the liquid, and it was confirmedthat a high quality image having an optical image density of 1.36 wasformed on the surface of the image supporting member.

The electrodeposition recording apparatus filled with theabove-described electrodeposition liquid of this example and the sameelectrodeposition recording apparatus filled with the electrodepositionliquid of Example 1 were allowed to stand as they were for 1 week. As aresult, the liquid surface of the electrodeposition recording apparatusof this example lowered by 25 mm, and the liquid surface of theelectrodeposition recording apparatus of Example 1 lowered only by 9 mm.Namely, it was confirmed that addition of wetting agents such asdiethylene glycol, isopropanol and the like was effective forpreservability of liquid property.

Example 8

The same electrodeposition liquid as in Example 1 was completed in thesame manner as in Example 1.

Then the same apparatus as in Example 2 as shown in FIG. 9 was used, andan image signal was inputted into an optical image inputting section onthe rear surface of the image supporting member by a He—Ne laser ray 23,while a pulse DC pulse voltage of 2.0 V (pulse widthe 2 ms/pulse cycle 3ms) was applied between the working electrode and the counter electrodeby means of the potentiostat power source 4. In this example, apropeller for stirring was inserted into the electrodeposition bath andthe image formation was conducted under the same conditions as inExample 2 with conducting slight stirring of the electrodepositionliquid in the bath.

Then the image supporting member which had completed this imageformation was taken out, and it was confirmed that an image having anoptical image density of 1.48 was formed on the surface of the imagesupporting member and the optical density distribution 6 at solid partwas 0.04. On the other hand, regarding the image formed in Example 1, itwas confirmed that an image having an optical image density of 1.42 wasformed on the surface of the image supporting member and the opticaldensity distribution δ at solid part was 0.09 in the same evaluations.Therefore, it was found that slight stirring of the electrodepositionliquid bath was useful for improving the optical image density anduniformity of and image.

Example 9

The same electrodeposition liquid as in Example 2 was completed in thesame manner as in Example 2.

Then the same apparatus as in Example 2 as shown in FIG. 9 was used, andan image signal was inputted into an optical image inputting section onthe rear surface of the image supporting member by a He—Ne laser ray 23,while a pulse DC pulse voltage of 2.5 V (pulse widthe 2 ms/pulse cycle 3ms). was applied between the working electrode and the counter electrodeby means of the potentiostat power source 4. In this example, atemperature control apparatus was inserted into the electrodepositionbath and the image formation was conducted at constant temperature (40°C.) with conducting temperature control.

Then the image supporting member which had completed this imageformation was taken out, and it was confirmed that an image having anoptical image density of 1.49 was formed on the surface of the imagesupporting member and the optical density distribution 6 at solid partwas 0.05. On the other hand, regarding the image formed in Example 2, itwas confirmed that an image having an optical image density of 1.48 wasformed on the surface of the image supporting member and the opticaldensity distribution 6 at solid part was 0.09 in the same evaluations.Therefore, it was found that control of the liquid temperature of thecoloring material liquid in the coloring material electrodepositionliquid bath at constant temperature was useful for improving the opticalimage density and uniformity of and image.

Example 10

According to the same manner as in Example 3, an electrodepositionliquid was prepared, the image forming process was conducted, the imagesupporting member on which an image had been formed was taken out fromthe electrodeposition bath, and plain paper was placed on the surface ofthe image supporting member on which an image containing the coloringmaterial particle had been formed.

A conductive rubber roller and insulated rubber roller were used, andthe plain paper and the image supporting member were sandwiched therebetween at a linear load of 300 g/cm by applying pressure and biasvoltage of +600 V was applied to the conductive rubber roller. The paperand the image supporting member were conveyed by the rotation of therollers. Directly after conveyed out from the rollers, the plain paperwas peeled from the image supporting member, and a transferred imagehaving an optical image density of 1.38 was formed on the plain paper.

Then, the remaining image forming material after the transfer on thesurface of the image supporting member was removed by using a rubberblade. By this, the surface of the image supporting member returned tothe initial condition, and preparation for the next image formation wasaccomplished. The critical surface tension on the surface of the imagesupporting member was 35 dyne/cm.

Example 11

The image forming process was conducted in a similar manner as inExample 3 except that an electrodeposition liquid was prepared accordingto the same manner as in Example 3, but an image supporting memberhaving a critical surface tension of 44 dyne/cm was used, and the imagesupporting member on which surface an image had been formed was takenout from the electrodeposition bath, and plain paper was placed on thesurface of the image supporting member on which an image containing thecoloring material particle had been formed.

A conductive rubber roller and insulated rubber roller were used, andthe plain paper and the image supporting member were sandwiched therebetween at a linear load of 300 g/cm by applying pressure and biasvoltage of +500 V was applied to the conductive rubber roller. The plainpaper and the image supporting member were conveyed by the rotation ofthe rollers. Directly after conveyed out from the rollers, the plainpaper was peeled from the image supporting member, and a transferredimage having an optical image density of 1.18 was formed on the plainpaper.

Then, the remaining image forming material after the transfer on thesurface of the image supporting member was removed by using a rubberblade. However, the image forming material partially remained in theform of a film, and the surface of the image supporting member did notreturn to the initial condition. By this, it was found that when thecritical surface tension on the surface of the image supporting memberis too high, the surface of the image supporting member does not easilyreturn to the initial condition, therefore, it is not suitable forre-use.

Example 12

The image forming process was conducted in a similar manner as inExample 2 except that an electrodeposition liquid was prepared accordingto the same manner as in Example 2, but an image supporting memberhaving a critical surface tension of 18 dyne/cm was used, and the imagesupporting member was taken out from the electrodeposition bath, acoloring material image was formed on the image supporting member andplain paper was placed on the surface of the image supporting member. Aconductive rubber roller and insulated rubber roller were used, and theplain paper and the image supporting member were sandwiched between therollers at a linear load of 300 g/cm by applying pressure and biasvoltage of +600 V was applied to the conductive rubber roller. The paperand the image supporting member were conveyed by the rotation of therollers. Directly after conveyed out from the rollers, the plain paperwas peeled from the image supporting member, and a transferred imagehaving an optical image density of 0.88 on solid part was formed on theplain paper. However, the line image generated flow and exhibitreproduction deficiency. By this, it was found that when the criticalsurface tension on the surface of the plain member of the imagesupporting member is too low, the maintaining ability of the imageformed on the surface of the image supporting member deteriorates.

Then, the remaining image forming material after the transfer on thesurface of the image supporting member was removed by using a rubberblade. By this, the surface of the image supporting member returned tothe initial condition, and preparation for the next image formation wasaccomplished.

Example 13

160 parts by weight of 20% by weight aqueous alkali solution of astyrene-methacrylic acid copolymer (molecular weight: 16,000,hydrophobic group/(hydrophilic group+hydrophobic group) molar ratio:69%, acid value: 160), 5 parts by weight of carbon black powder (havingan average particle diameter of 0.1 μm), 15 parts by weight ofdiethylene glycol, 7 parts by weight of isopropanol, and 55 parts byweight of distilled water were mixed, and moderately stirred for 1 hourby means of a propeller to sufficiently wet the carbon black powder withthe liquid and thus to prepare a dispersion containing roughly dispersedcarbon black powder. This dispersion was then subjected to an intensive,forced-dispersing treatment using a homogenizer for 3 minutes to preparea base dispersion. Into this base dispersion was dropwisely added adilute solution containing 120 parts by weight of distilled water, 10parts by weight of glycerin, and 0.3 parts by weight of an anti-moldagent ((Proxycel XL-2 manufactured by ICI Inc.) while the liquid wasstirred with a propeller. In this way, an electrodeposition liquid wasprepared. The pH of this liquid was set to 4.6, 6.0, 7.5 and 9.5,respectively, by adjusting pH the using an aqueous solution ofhydrochloric acid and an aqueous solution of sodium hydroxide. The pH atwhich the fine particles of the coloring material started depositionfrom the liquid was 5.0. The pH at which precipitation leaving acomplete supernatant occurred was 4.4.

Then, as illustrated in FIG. 4, in an electrodeposition bath 2 filledwith the electrodeposition liquid 1 was disposed an image supportingmember 3, whose rear surface was fitted with a working electrode so thatan image signal could be inputted, in such a manner that the rearsurface was exposed to the outside of the bath. Further, in the bath 2were disposed a counter electrode 5 and a controlling electrode 6utilizing a salt bridge. The image supporting member 3 had amultilayered structure comprising a 4 mm thick blue glass platesubstrate having a transparent electrically conductive layer of ITOformed thereon, and the transparent electrically conductive layer wascovered with two organic photoconductive layers. The electricallyconductive layer of ITO functioned as a working electrode and thesurface of the organic photoconductive layer was smooth. The respectiveelectrodes were connected to a potentiostat power source. An imagesignal was inputted into an optical image inputting section on the rearsurface of the image supporting member while a DC voltage of 2.6 V wasapplied between the working electrode and the counter electrode for 7seconds by means of the potentiostat power source.

Next, the image supporting member which had completed this imageformation procedure was withdrawn from the liquid, and it was confirmedthat high quality images having an optical image density of 1.35(electrodeposition liquid of pH 4.6), 1.43 (electrodeposition liquid ofpH 6.0), 1.39 (electrodeposition liquid of pH 7.5) and 1.05(electrodeposition liquid of pH 9.5). In the electrodeposition liquid ofpH 4.6, the coloring particle was precipitated at the bottom of thebath, and dispersion condition was instable.

As described above, according to the image recording method of thepresent invention, image formation is carried out by depositionphenomenon of an electrodeposition material containing a coloringparticle onto an image supporting member which can allow currentcorresponding to an image signal through an electrodeposition liquidcontaining the above-described electrodeposition material, and imageformation can be effected at given position by application of voltageand irradiation with a laser ray. Therefore, according to the presentinvention, recording can be conducted with excellent resolution, as wellas, recording can be achieved having printing properties such as highoptical density, high resolution, image structure having small imagethickness, strong adhesion of an image, excellent halftone reproduction,high fastness of an image, high safety and the like.

As described above, according to the inventions described in Examples 1to 13, an image having a high optical density, high resolution,structure of small thickness, high fastness and high safety can beachieved by conducting image formation by electrodeposition phenomenonusing an image supporting member wherein the proportion of the number ofhydrophobic groups in the monomer unit of an electrodeposition materialto the total number of hydrophilic groups and hydrophobic groups is inthe range from 40% to 80%, the average molecular weight of theelectrodeposition material is in the range from 4,000 to 30,000, theacid value is in the range from 60 to 300, and pH range in which aprecipitation is formed from dissolved condition in the change in pH ofan electrodeposition liquid is preferably 1 or less, and current isallowed to flow corresponding to an image signal.

Example 14

10 parts by weight of carbon black powder (having an average particlediameter of 0.1 μm), 15 parts by weight of diethylene glycol, 3 parts byweight of polyoxyethylene alkylether carboxylate, 3 parts by weight ofpolyethylene glycol dicarboxylate, 6 parts by weight of a water-solubleacrylic resin, 7 parts by weight of isopropanol, 2.0 parts by weight of20% by weight ammonia water, and 55 parts by weight of distilled waterwere mixed, and moderately stirred for 1 hour by means of a propeller tosufficiently wet the carbon black powder with the liquid and thus toprepare a dispersion containing roughly dispersed carbon black powder.This dispersion was then subjected to an intensive, forced-dispersingtreatment using a homogenizer for 3 minutes to prepare a basedispersion. Into this base dispersion was dropwisely added a dilutesolution containing 120 parts by weight of distilled water, 10 parts byweight of glycerin, and 0.8 parts by weight of an anti-mold agent((Proxycel XL-2 manufactured by ICI Inc.) while the liquid was stirredwith a propeller. In this way, a dispersion containing fine particles ofa coloring material for use in electrodeposition was prepared. The pH ofthis liquid was set to 7.5 by adjusting pH using an aqueous solution ofacetic acid (boiling point: 118° C.) and an aqueous solution of ammonia(boiling point: −33.4° C.).

The pH at which the fine particles of the coloring material starteddeposition from the liquid was 6.0. The resistivity of the liquid was7×10² Ω·cm.

In the image recording apparatus as illustrated in FIG. 4, this aqueouscoloring material liquid was used to record an image. As shown in FIG.4, in an electrodeposition bath 2 filled with the electrodepositionliquid 1 was disposed an image supporting member 3, whose rear surfacewas fitted with a working electrode so that an image signal could beinputted, in such a manner that the rear surface was exposed to theoutside of the bath. Further, in the bath 2 were disposed a counterelectrode 5 and a controlling electrode 6 utilizing a salt bridge. Theimage supporting member 3 had a multilayered structure comprising a 4 mmthick glass plate substrate having a transparent electrically conductivelayer of ITO formed thereon, and the transparent electrically conductivelayer was covered with two organic photoconductive layers(Perylene-phthalocyanine-based organic photoconductive layer). Theelectrically conductive layer of ITO functioned as a working electrodeand the surface of the organic photoconductive layer was smooth withoutunevenness. The respective electrodes were connected to a potentiostatpower source. An image signal was inputted into an optical imageinputting section on the rear surface of the image supporting member,while a DC voltage of 2.8 V was applied between the working electrodeand the counter electrode for 17 seconds by means of the potentiostatpower source.

Next, the image supporting member which had completed this imageformation was withdrawn from the liquid, and the liquid component andammonia component were removed from the deposited image by using a dryerat 130° C. for 30 seconds, and it was confirmed that an image having anoptical image density of 1.31 was formed on the surface of the imagesupporting member. The surface of this image was washed with distilledwater for 30 seconds. As a result, the optical image density of 1.31remained and high fastness was confirmed.

Example 15

20 parts by weight of carbon black powder (having an average particlediameter of 0.05 μm), 10 parts by weight of polyethylene glycol, 6 partsby weight of polymethyl acrylate dicarboxylate, 6 parts by weight ofpolyoxyethylene alkylphenylcarboxylate, 6 parts by weight of awater-soluble acrylic resin, 10 parts by weight of isopropanol, 6 partsby weight of an aqueous ammonia solution, and 50 parts by weight ofdistilled water were mixed, and moderately stirred for 3 hours by meansof a propeller to sufficiently wet the carbon black powder with theliquid and thus to prepare a dispersion containing roughly dispersedcarbon black powder. This dispersion was then subjected to a dispersingtreatment using a ball mill for 24 hours to prepare a base dispersion.Into this base dispersion was dropwisely added a diluent containing 200parts by weight of distilled water, 20 parts by weight of glycerin and0.5 parts by weight of an anti-mold agent ((Proxycel XL-2 manufacturedby ICI Inc.) while the liquid was stirred with a propeller. In this way,a dispersion containing fine particles of a coloring material for use inelectrodeposition was prepared. The pH of this liquid was set to 7.0 byadjusting pH by an aqueous solution of hydrochloric acid (boiling point:−85° C.) and an aqueous solution of ammonia (boiling point: −33.4° C.).

The pH at which the fine particles of the coloring material starteddeposition from the liquid was 5.5. The resistivity of the liquid was5×10² Ω·cm.

Using an image recording apparatus as illustrated in FIG. 9, in a bath 2filled with the electrodeposition liquid was disposed an imagesupporting member 3, whose rear surface was fitted with a workingelectrode so that an image signal could be inputted, in such a mannerthat the rear surface was exposed to the outside of the bath. Further,in the bath 2 were disposed a counter electrode 5 and a controllingelectrode 6 utilizing a salt bridge. The image supporting member 3 had amultilayered structure comprising a 2 mm thick quartz substrate having atransparent electrically conductive layer of ITO formed thereon, and thetransparent electrically conductive layer was covered with two organicphotoconductive layers from by a similar manner as in Example 14. Theelectrically conductive layer of ITO functioned as a working electrodeand the surface of the organic photoconductive layer was smooth. Therespective electrodes were connected to a potentiostat power source. Animage signal was inputted into an optical image inputting section on therear surface of the image supporting member by a He—Ne laser ray 23emitted from a laser source 24, while a DC pulse voltage of 4.0 V(having a pulse width of 2 ms/pulse cycle of 3 ms) was applied betweenthe working electrode and the counter electrode by means of thepotentiostat power source 4.

Next, the image supporting member which had completed this imageformation was withdrawn from the liquid, smooth plain paper was placedon the surface of the image supporting member, and passed through a pairof aluminum rolls coated with silicone rubber under pressed condition atthe surface temperature thereof of 150° C., and an image is heated andtransferred to this plain paper and simultaneously the ammonia componentwas removed by this heating. It was confirmed that a high quality imagehaving an optical image density of 1.28 was formed on the surface of theimage supporting member. For testing water-resistance of this imagerecorded paper, it was immersed in pure water at 40° C. for 60 secondsand change between before and after the immersion was evaluated. As aresult, it was found that the change in the optical image density was0.1 or less, and the recorded paper had high water-resistance andfastness.

Example 16

10 parts by weight of phthalocyanine powder (having an average particlediameter of 0.05 μm), 10 parts by weight of ethyl cellosolve, 7 parts byweight of polyoxyethylene alkylphenylacetate, 4 parts by weight ofpolymethyl acrylate dicarboxylate, 6 parts by weight of a water-solubleacrylic resin, 10 parts by weight of isopropanol, 4 parts by weight ofdimethtylaminoethanol and 50 parts by weight of distilled water weremixed, and moderately stirred for 0.5 hours by means of a propeller tosufficiently wet the pigment powder with the liquid and thus to preparea dispersion containing roughly dispersed pigment powder. Thisdispersion was then subjected to a dispersing treatment using ahomogenizer for 6 minutes to prepare a base dispersion. Into this basedispersion was dropwisely added a dilute solution containing 170 partsby weight of distilled water, 30 parts by weight of diethylene glycoland 0.5 parts by weight of an anti -mold agent ((Proxycel XL-2manufactured by ICI Inc.) while the liquid was stirred with a propeller.In this way, a dispersion containing fine particles of a coloringmaterial for use in electrodeposition was prepared. The pH of thisliquid was set to 7.6 by adjusting the pH using an aqueous solution ofhydrochloric acid (boiling point: −85° C.) and an aqueous solution ofdimethylaminoethanol (boiling point: 135° C.). The pH at which the fineparticles of the coloring material starting deposition from the liquidwas 6.0. The volume resistivity of the liquid was 5×10² Ω·cm.

Using the image recording apparatus as illustrated in FIG. 10, in a bath2 filled with the electrodeposition liquid was disposed an imagesupporting member 3 to which an image signal could be inputted, in sucha manner that the rear surface was exposed to the outside of the bath.The image supporting member 3 gave a conductive layer of 5 mm thick inwhich current scattering had been suppressed and the surface in contactwith the liquid of the conductive layer was smooth. The respectiveelectrodes were connected to a potentiostat power source. An imagesignal was inputted into an image inputting section on the rear surfaceof the image supporting member using a needle electrode image inputtingprinting head 12 of 600 DPI, while a DC pulse voltage of 10.0 V (pulsewidth 2 ms/pulse cycle 3 ms) was applied between the needle electrodeand the counter electrode in synchronization with the scanning speed ofthe printing head 28.

Next, the image supporting member which had completed this imageformation was withdrawn from the liquid and dried with hot air at 10° C.for 30 seconds, and it was confirmed that a cyan-colored high qualityimage having an optical image density of 1.43 was formed on the surfaceof the image supporting member. Further, printing was conducted, while aDC pulse voltage of 6.5 V was applied between the needle electrode andthe counter electrode and hot air drying was conducted in the samemanner, and it was confirmed that a cyan-colored high quality imagehaving an optical image density of 1.10 was formed on the surface of theimage supporting member.

By this, it was found that the optical image density of the resultingimage can be controlled by controlling the voltage applied.

Example 17

20 parts by weight of carbon black powder (having an average particlediameter of 0.02 μm), 10 parts by weight of polyethylene glycol, 5 partsby weight of polymethyl acrylate dicarboxylic acid, 5 parts by weight ofpolyoxyethylenealkylphenyl carboxylic acid, 6 parts by weight of awater-souble acrylic resin, 10 parts by weight of isopropanol, 3 partsby weight of methylaminoethanol, and 50 parts by weight of distilledwater were mixed, and moderately stirred for 3 hours by means of apropeller to sufficiently wet the carbon black powder with the liquidand thus to prepare a dispersion containing roughly dispersed carbonblack powder. This dispersion was then subjected to a dispersingtreatment using a ball mill for 24 hours to prepare a base dispersion.Into this base dispersion was dropwise added a dilute solutioncontaining 200 parts by weight of distilled water, 20 parts by weight ofglycerin, 4 parts by weight of pyrrole and 0.5 parts by weight of ananti-mold agent ((Proxycel XL-2 manufactured by ICI Inc.) while theliquid was stirred with a propeller. In this way, a dispersioncontaining fine particles of a coloring material for use inelectrodeposition was prepared. The pH of this liquid was set to 6.7 byadjusting pH using an aqueous solution of phosphoric acid and an aqueoussolution of methylaminoethanol. The pH at which the fine particles ofthe coloring material started deposition from the liquid was 5.0. The pHat which precipitation leaving a clear supernatant occurred was 5.4. Theresistivity of the liquid was 3×10² Ω·cm.

The same apparatus as in Example 15 as illustrated in FIG. 9 was used,and, in an electrodeposition bath 2 filled with the electrodepositionliquid 1 was disposed an image supporting member 3, whose rear surfacewas fitted with a working electrode so that an image signal could beinputted, in such a manner that the rear surface was exposed to theoutside of the bath. Further, in the bath 2 were disposed a counterelectrode 5 and a controlling electrode 6 utilizing a salt bridge. Theimage supporting member 3 had a multilayered structure comprising a 2 mmthick plate quartz substrate having a transparent electricallyconductive layer of ITO formed thereon, and the transparent electricallyconductive layer was covered with two organic photoconductive layers.The electrically conductive layer of ITO functioned as a workingelectrode and the surface of the organic photoconductive layer wassmooth. The respective electrodes were connected to a potentiostat powersource. An image signal was inputted into an optical image inputtingsection on the rear surface of the image supporting member by a He—Nelaser ray, while a DC pulse voltage of 3.0 V was applied between theworking electrode and the counter electrode by means of the potentiostatpower source 4.

Next, the image supporting member which had completed this imageformation was withdrawn from the liquid, smooth plain paper was placedon the surface having the image of the image supporting member andtransfer by applying pressure was conducted onto the plain paper and thetransferred image was passed through a pair of aluminum rolls coatedwith silicone rubber under a linear pressure of 300 g/cm at the surfacetemperature thereof of 160° C., and removal of the amine component andfixation of the image on this plain paper was conducted. It wasconfirmed that a high quality image having an optical image density of1.26 was formed on the surface of the plain paper. This image wasimmersed in water in a water tank to which ultrasonic vibration wasapplied for 30 seconds. As a result, it was found that the change in theimage density was 0.1 or less, and the recorded paper had highwater-resistance and fastness.

As described above, according to the inventions described in Examples 14to 17, an image having high optical density, high resolution, structureof small thickness, excellent half-tone reproduction, high fastness andhigh safety can be obtained by conducting image formation byelectrodeposition phenomenon on an image supporting member whereincurrent is allowed to flow corresponding to an image signal, using anaqueous electrodeposition material dispersion containing a pH regulatorhaving a boiling point of 150° C. or less, and by removing, in thesubsequent image heating process, only the pH regulator, orparticularly, a pH regulator which promotes deterioration anddissolution of the image.

What is claimed is:
 1. An image forming method, comprising: preparing anaqueous dispersion containing an electrodeposition material in a liquidin a vessel, the electrodeposition material including: a fine particlecoloring material; and a polymer which is chemically dissolved, anddeposited or precipitated by change in pH, wherein the vessel havingtherein: an image supporting member including at least: an electrode,which can supply current or an electric field in accordance with animage pattern, and a surface which can support an image; and a counterelectrode which forms a pair of electrodes together with the electrode;depositing and precipitating the electrodeposition material to form animage by supplying current or an electric field in accordance with animage pattern to the image supporting member and the counter electrodeand by changing the pH value of the aqueous dispersion in the vicinityof the image supporting surface of the image supporting member; whereinthe polymer included in the electrodeposition material comprises bothhydrophobic groups and hydrophilic groups in the molecule, theproportion of the number of the hydrophobic groups to the total numberof hydrophobic groups and hydrophilic groups in the polymer is in therange of from 40% to 80%, 50% or more of the hydrophilic groups canreversibly change from hydrophilic groups to hydrophobic groups due to achange in pH value, and the acid value of the polymer is in the range offrom 30 to
 400. 2. An image forming method according to claim 1, furthercomprising the step of: transferring and fixing, onto a recordingmedium, the electrodeposition material which has been deposited andprecipitated in an image pattern on the image supporting surface of theimage supporting member.
 3. An image forming meth od according to claim2, wherein the current or electric field is supplied to the imagesupporting member and the counter electrode by a current generatingmeans for generating current on the image supporting surface of theimage supporting member in accordance with a photoimage signal, thecurrent generating means including a mechanism for converting aninputted photoimage signal into current.
 4. An image forming methodaccording to claim 1, wherein the hydrophilic groups which can changereversibly to hydrophobic groups from hydrophilic groups due to a changein pH each have a carboxyl group or an amino group.
 5. An image formingmethod according to claim 4, wherein the hydrophobic groups each containat least one of a styrene unit an α-methylstyrene unit and.
 6. An imageforming method according to claim 2, wherein the average particle sizeof the fine particle coloring material is in the range from 0.02 μm to0.3 μm.
 7. A colored film formed on a substrate by the method as setforth in claim
 1. 8. An image forming material for use in an imageforming method, the image forming material comprising an aqueousdispersion containing an electrodeposition material including: a fineparticle coloring material; and a polymer which is chemically dissolved,or is deposited and precipitated, by a change in pH, and the aqueousdispersion is prepared in a liquid in a vessel and the vessel havingtherein: an image supporting member including at least: an electrodewhich can supply current or an electric field in accordance with animage pattern, and a surface which can support an image; and a counterelectrode which forms a pair of electrodes together with the electrode;wherein the electrodeposition material is deposited and precipitated toform an image by supplying current or electric field in accordance withan image pattern to the image supporting member and the counterelectrode and by changing the pH value of the aqueous dispersion in thevicinity of the image supporting surface of the image supporting member;wherein the polymer included in the electrodeposition material has bothhydrophobic groups and hydrophilic groups in the molecule, theproportion of the number of the hydrophobic groups to the total numberof the hydrophobic groups and hydrophilic groups in the polymer is inthe range of from 40% to 80%, 50% or more of the hydrophilic groups canreversibly change from hydrophilic groups to hydrophobic groups due to achange in pH value, and the acid value of the polymer is in the range offrom 30 to
 400. 9. An image forming material according to claim 8,wherein: (i) when the electrodeposition material is deposited on ananode during electrodeposition, the pH value of said aqueous dispersionis set within the range from a pH value, which equals a start pH valueat which electrodeposition of the electrodeposition material startsminus the number 1, to a pH value which equals the start pH value plusthe number 3, and (ii) when the electrodeposition material is depositedon a cathode during electrodeposition, the pH value of said aqueousdispersion is set within the range from a pH value which equals thestart pH value minus the number 3, to a pH value which equals the startpH value plus the number 1.